BNZ Materials Bazelite 2300 LI Insulating Castable

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name	Bazelite
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials Bazelite 2300 LI Insulating Castable.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Blaz 2300 L is similar to Blaz 2300 but suitable for those applications where reducing conditions might be encountered. These high purity, low iron products are specifically designed for both back-up and exposed to furnace combustion.Information provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	0.977 g/cc	0.0353 lb/in³	Fired at 5 hrs at 816°C

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.000340 GPa @Temperature 1095 °C	0.0493 ksi @Temperature 2003 °F	ASTM C268
	0.000400 GPa @Temperature 815 °C	0.0580 ksi @Temperature 1500 °F	ASTM C268
	0.000620 GPa @Temperature 1260 °C	0.0899 ksi @Temperature 2300 °F	ASTM C268
	0.000900 GPa @Temperature 104 °C	0.131 ksi @Temperature 219 °F	Dried; ASTM C268
	0.00103 GPa @Temperature 540 °C	0.149 ksi @Temperature 1000 °F	Fired; ASTM C268
Compressive Strength	2.21 MPa @Temperature 1095 °C	320 psi @Temperature 2003 °F	Cold Crush Strength
	2.83 MPa @Temperature 815 °C	410 psi @Temperature 1500 °F	Cold Crush Strength
	2.96 MPa @Temperature 1260 °C	430 psi @Temperature 2300 °F	Cold Crush Strength
	2.83 MPa @Treatment Temp. 540 °C	410 psi @Treatment Temp. 1000 °F	Cold Crush Strength; Dried 104°C
	4.83 MPa @Treatment Temp. 104 °C	700 psi @Treatment Temp. 219 °F	Cold Crush Strength; Dried 104°C

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	1260 °C	2300 °F
Shrinkage	0.10 % @Temperature 540 °C	0.10 % @Temperature 1000 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 815 °C	0.20 % @Temperature 1500 °F	Permanent Linear Change; ASTM C210
	0.40 % @Temperature 1095 °C	0.40 % @Temperature 2003 °F	Permanent Linear Change; ASTM C210
	1.0 % @Temperature 1260 °C	1.0 % @Temperature 2300 °F	Permanent Linear Change; ASTM C210

Component Elements Properties	Metric	English	Comments
Al2O3	41.3 %	41.3 %
CaO	14.1 %	14.1 %
Fe2O3	0.90 %	0.90 %
MgO	0.20 %	0.20 %
Na2O	1.2 %	1.2 %	Includes K<sub>2</sub>O
SiO2	41 %	41 %
TiO2	1.6 %	1.6 %