BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldability and outstanding surface appearance.

Physical Properties	Metric	English	Comments
Density	1.74 g/cc	0.0629 lb/in³	dry; ISO 1183
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	155 MPa	22500 psi	5mm/min; ISO 527
Tensile Modulus	13.4 GPa	1940 ksi	1mm/min; ISO 527

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Descriptive Properties	Value	Comments
Color	BK-102
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes