BASF Novolen® 3200 H Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 3200 H Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Blow moldings and thermoformed parts.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 2.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 12 % | 12 % | |
| Tensile Modulus | 0.900 GPa | 131 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | |
| 0.180 J/cm² @Temperature -30.0 °C |
0.857 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 185 µm/m-°C @Temperature 20.0 °C |
103 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 145 °C | 293 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 65.0 °C | 149 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.3 @Frequency 100 Hz |
2.3 @Frequency 100 Hz |
|
| 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.000070 @Frequency 100 Hz |
0.000070 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Pau Tai Unistab BZ-591 Mixed Metal Liquid Stabilizer for PVC Barium/Zinc Self-Lubricating
- ExxonMobil Exceed™ 1018 FA Blown Film Resin (discontinued **)
- Fiberfil® J-60/40/E Polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled
- Sinotek Materials ZSLZ89 Middle Carbon Graphite
- Teknor Apex Sinvicomp SIM 6019 Polyvinyl Chloride, Flexible
- A. Schulman POLYFORT™ PP 7001
- Zhejiang Juner PC-A7 Top-Grade Flame Retardant UV-Resistant
- DuPont™ Nomex® 430 1600 Denier Aramid Yarn
- Huntsman PE2053 Injection Molding Polyethylene (discontinued **)
- Unipetrol PE HD LITEN® MB/ML 71 HDPE
Copyright © lookpolymers.com All Rights Reserved