BASF Novolen® 2348 TC Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 2348 TC Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Grade with nucleating and antistatic agents for injection molded parts.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 65 g/10 min @Load 2.16 kg, Temperature 230 °C |
65 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | |
| Elongation at Break | 40 % | 40 % | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| Tensile Modulus | 1.35 GPa | 196 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | |
| 0.250 J/cm² @Temperature -30.0 °C |
1.19 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 163 °C | 325 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | |
| Vicat Softening Point | 70.0 °C | 158 °F | |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | |
| Dielectric Constant | 2.3 @Frequency 100 Hz |
2.3 @Frequency 100 Hz |
|
| 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.00081 @Frequency 100 Hz |
0.00081 @Frequency 100 Hz |
|
| 0.0020 @Frequency 1e+6 Hz |
0.0020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Outokumpu 4028 Martensitic Stainless Steel
- PolyOne Geon™ Vinyl Flexible R4294Y Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kaiser 6033 T8 Rod & Bar
- Teknor Apex APEX® 2085-H Polyvinyl Chloride, Flexible
- Styrolution Novodur® 240 ABS
- Axiall 8881 Moldings & Extrusions Flexible PVC
- Addcomp ADD-VANCE® UV 51 20% active PP based anti-UV masterbatch
- BASF Luranyl® KR 2451/3 Polyphenylene Ether + Styrene-Butadiene Blend
Copyright © lookpolymers.com All Rights Reserved