BASF Luranyl® KR 2454/3 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled , Styrene-Butadiene
Manufacturer	BASF
Trade Name	Luranyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Luranyl® KR 2454/3 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Heat resistant grade with halogen-free flame retardant; applications include TV plug connectors and components in switchgear cabinets.Data was collected by ISO methods and provided by BASF.

Physical Properties	Metric	English
Density	1.16 g/cc	0.0419 lb/in³
Water Absorption	0.40 %	0.40 %
Moisture Absorption at Equilibrium	0.15 %	0.15 %
Linear Mold Shrinkage, Flow	0.0045 cm/cm	0.0045 in/in
High Load Melt Index	24 g/10 min @Load 21.6 kg, Temperature 250 °C	24 g/10 min @Load 47.6 lb, Temperature 482 °F

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	75.0 MPa	10900 psi
Elongation at Break	4.0 %	4.0 %
Tensile Modulus	4.50 GPa	653 ksi
Charpy Impact Unnotched	3.50 J/cm²	16.7 ft-lb/in²
	3.50 J/cm² @Temperature -30.0 °C	16.7 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.10 J/cm²	5.24 ft-lb/in²
	1.10 J/cm² @Temperature -30.0 °C	5.24 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	45.0 µm/m-°C @Temperature 20.0 °C	25.0 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F
Deflection Temperature at 1.8 MPa (264 psi)	133 °C	271 °F
Vicat Softening Point	138 °C	280 °F
Flammability, UL94	V-1 @Thickness 3.20 mm	V-1 @Thickness 0.126 in
Oxygen Index	29 %	29 %

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.8 @Frequency 100 Hz	2.8 @Frequency 100 Hz
	2.8 @Frequency 1e+6 Hz	2.8 @Frequency 1e+6 Hz
Dielectric Strength	85.0 kV/mm	2160 kV/in
Dissipation Factor	0.0030 @Frequency 1e+6 Hz	0.0030 @Frequency 1e+6 Hz
Comparative Tracking Index	225 V	225 V