- Polytetrafluoroethylene (PTFE), Glass Filled, Molded
- Azoty Tarnow™ TARFLEN SM-S25 PTFE
Azoty Tarnow™ TARFLEN SM-S25 PTFE
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARFLEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARFLEN SM-S25 PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tarflen SM1 reinforced with 25% glass fiber for standard compression molding.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.24 g/cc | 0.0809 lb/in³ | ISO 1183 |
| Filler Content | 25 % | 25 % | Glass Fibers |
| Particle Size | 40 µm | 40 µm | Average |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ISO 868 |
| Ball Indentation Hardness | 38.0 MPa | 5510 psi | ISO 2039-1 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527 |
| Elongation at Break | 260 % | 260 % | ISO 527 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C |
36.1 µin/in-°F @Temperature 68.0 °F |
ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.90e+13 ohm | 1.90e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.1 | 2.1 | IEC 60250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.42 | 0.42 | IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 50.0 - 70.0 MPa | 7250 - 10200 psi | Molding Pressure |
Users viewing this material also viewed the following:
- Radici Radilon® ACP300 K (dry) Nylon 66
- Polyplastic Armlen® PP MF 30-3IM Polypropylene, 30% Mineral Filled
- MarkeTech Aluminum Oxide Ceramic - Alumina 99.5%
- SABIC Innovative Plastics LNP LUBRICOMP RCL36 PA 66
- Hexcel® HexForce™ XLS9102 Carbon/Wire Fabric
- ExxonMobil LLDPE LL 6201XR Wire & Cable Linear Low Density Polyethylene Resin (European Grade)
- DuPont Performance Polymers Zytel® PLS FR95G15DH2 BK269 Nylon 6
- Fainplast Compounds Hax™ HFC 0108/4 Flame Retardant Polyolefin Cable Compound
- Buckeye Polymers BP RPP 4010 T NAT Polypropylene, Talc Filled
- Overview of materials for Nylon 6, 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved