| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 527-33G Nylon 66, 33% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A 33% glass reinforced impact modified Nylon 66.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | ATSM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 252 °C | 486 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | ASTM D648 |
Users viewing this material also viewed the following:
- DuPont 20 Series 2020 Specialty Polyethylene Resin (discontinued **)
- Materion BrushCAST® 275CT Fine Grain Casting Alloy (As Cast)
- Techmer ES HiFill® PA6/6 GF20 HS BK 20% Glass Filled
- A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product
- CIMBAR FlexTalc® 1222D Ultrafine Talc for TPO Applications, Densified
- Barlog Plastics KEBATER BF250 PBT, 50% glass fiber reinforced, food grade
- LNP Lubricomp® IBL-4416 Polyamide 6/12 Copolymer, Glass Bead Reinforced, Silicone Lubricant (discontinued **)
- A. Schulman POLYBATCH™ Red 5330 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved