Arkema Group LOTRYL® 35 BA 40 Copolymer Ethylene - Butyl Acrylate

Category	Polymer , Thermoplastic , Ethylene Butyl Acrylate
Manufacturer	Arkema
Trade Name	LOTRYL®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group LOTRYL® 35 BA 40 Copolymer Ethylene - Butyl Acrylate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LOTRYL® 35 BA 40 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. Co-monomer content is 35% in weight. LOTRYL® 35 BA 40 is particularly recommended for the formulation of hot melt adhesives.Information provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	0.930 g/cc @Temperature 23.0 °C	0.0336 lb/in³ @Temperature 73.4 °F	ISO 1183
Butyl Acrylate Content	32 - 37 %	32 - 37 %	IRTF (internal)
Melt Index of Compound	35 - 45 g/10 min @Load 2.16 kg, Temperature 190 °C	35 - 45 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	70	70	ASTM D2240
Tensile Strength at Break	2.00 MPa	290 psi	ASTM D638
Elongation at Break	300 %	300 %	ASTM D638

Thermal Properties	Metric	English	Comments
Melting Point	66.0 °C	151 °F	DSC
Vicat Softening Point	<= 40.0 °C @Load 1.02 kg	<= 104 °F @Load 2.25 lb	ASTM D1525
Ring & Ball Softening Point	110 °C	230 °F	ASTM E28

Processing Properties	Metric	English	Comments
Processing Temperature	<= 300 °C	<= 572 °F