Aremco Ceramabond™ 835-M High Temperature Ceramic Adhesive/Paste, Alumina Filled

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Aremco
Trade Name Ceramabond™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aremco Ceramabond™ 835-M High Temperature Ceramic Adhesive/Paste, Alumina Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: High Strength, Good Filler Bonding: Ceramic to Ceramic, Ceramic to Metal Principal Use: Halogen Lamps
Physical Properties Metric English Comments
Density 2.35 - 2.45 g/cc
0.0849 - 0.0885 lb/in³
Volatile Organic Compounds (VOC) Content 0.000 g/l
0.000 g/l
Viscosity 30000 - 40000 cP
30000 - 40000 cP
Mechanical Properties Metric English Comments
Impact Test 85.4 J
63.0 ft-lb
Torque Strength; curing at 1000°F
Thermal Properties Metric English Comments
CTE, linear 7.20 µm/m-°C
4.00 µin/in-°F
Maximum Service Temperature, Air 1650 °C
3000 °F
Electrical Properties Metric English Comments
Dielectric Strength 6.42 kV/mm
163 kV/in
Processing Properties Metric English Comments
Processing Temperature 50.0 - 90.0 °C
122 - 194 °F
Application Temp
Cure Time 120 min

@Temperature 93.3 °C
2.00 hour

@Temperature 200 °F
preceeded by 1-4 hour air set
Shelf Life 6.00 Month

@Temperature 4.44 - 32.2 °C
6.00 Month

@Temperature 40.0 - 90.0 °F
Descriptive Properties Value Comments
Acid Resistance Good
after curing at 700°F for 2 hours
Alkali Resistance Excellent
after curing at 700°F for 2 hours
Color White
Moisture Resistance Good
after curing at 700°F for 2 hours
Solvent Water
Thinner 835-M-T