Category | Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE |
Manufacturer | AlphaGary |
Trade Name | Evoprene™ LF |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | AlphaGary Evoprene™ LF 6160 Automotive Thermoplastic Elastomer.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.04 g/cc | 1.04 g/cc | ISO 1183 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 95 | 95 | ISO 868, 15 sec |
Tensile Strength | 17.6 MPa | 2550 psi | 500 mm/min, measured parallel to flow; ISO 37 |
Elongation at Break | 390 % | 390 % | 500 mm/min, measured parallel to flow; ISO 37 |
100% Modulus | 0.0135 GPa | 1.96 ksi | 500 mm/min, measured parallel to flow; ISO 37 |
Tear Strength | 81.0 kN/m | 462 pli | Parallel to flow; ISO 34-B |
104 kN/m | 593 pli | Perpendicular to flow; ISO 34-B | |
Tensile Set | 95 % @Temperature 70.0 °C, Time 79200 sec |
95 % @Temperature 158 °F, Time 22.0 hour |
VDA 675 217B |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 165 °C @Time 10800 sec |
329 °F @Time 3.00 hour |
no distortion |
Brittleness Temperature | -21.0 °C | -5.80 °F | ASTM D 746 |
Flame Spread | 51 mm/min | 2.0 in/min | burn rate |
Descriptive Properties | Value | Comments |
---|---|---|
Fogging, Reflectance % | SAE J 1756 | |
Odor rating | 2 | SAE J1351 / FLTM BO131-01 (dry) |
Ozone Resistance | 0 | 100 pphm / 200 hrs / 20% strain |