Alliance N-50 Neodymium Iron Boron Magnetic Material
| Category | Metal , Electronic/Magnetic Alloy , Ferrous Metal , Ferritic |
| Manufacturer | Alliance LLC |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Alliance N-50 Neodymium Iron Boron Magnetic Material.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.50 - 7.80 g/cc | 0.271 - 0.282 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Vickers | 570 - 580 | 570 - 580 | |
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
| Compressive Strength | 850 - 1050 MPa | 123000 - 152000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 5.00 µm/m-°C @Temperature 20.0 °C |
2.78 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
| CTE, linear, Transverse to Flow | -1.00 µm/m-°C @Temperature 23.0 °C |
-0.556 µin/in-°F @Temperature 73.4 °F |
|
| Specific Heat Capacity | 0.440 J/g-°C | 0.105 BTU/lb-°F | |
| Thermal Conductivity | 9.00 W/m-K | 62.5 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000120 - 0.000160 ohm-cm | 0.000120 - 0.000160 ohm-cm | |
| Magnetic Coercive Force, Hc | 10500 Oe | 10500 Oe | |
| 12000 Oe | 12000 Oe | Intrinsic | |
| Magnetic Remanence, Br | 14200 Gauss | 14200 Gauss | |
| Magnetic Maximum Energy Product, BH | 47 - 51 MGOe | 47 - 51 MGOe | |
| Curie Temperature | 310 °C | 590 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Reversible Temp Coef., Bd | -0.12 %/°C | |
| Reversible Temp Coef., Hd | -0.60 %/°C | |
| Temperature Coefficient, Br | -0.11 %/°C | (20-100°C) |
| Temperature Coefficient, Hci | -0.72 %/°C | (20-100°C) |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-MASK II HT Conductive Foil Tape
- SABIC Innovative Plastics Lexan® EXL1414T PC Copolymer
- Overview of materials for Solventless Epoxy Varnish, Electrical Insulation
- Gromax CCP PBT 1100-211X
- Shinkong Synthetic Fibers Shinite® D202G15 PBT, 15% Glass Filled, Fire Retardant
- A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene
- Ametek Tungsten-Copper Composites AWC 9010
- Polyplastic Armamid® PA6 GF 30 HS-901 Nylon, 30% Glass Filled
- Haynes 25 alloy, room temperature after 20% cold reduction
- Victrex® Vicote® 704 Polyetheretherketone (PEEK) Powder
Copyright © lookpolymers.com All Rights Reserved