Adamas Adalon® 415 PTFE, 10% Organic Filler
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 415 PTFE, 10% Organic Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 - 1.92 g/cc | 1.85 - 1.92 g/cc | ASTM D792 |
| Deformation | 2.7 - 3.0 % | 2.7 - 3.0 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 - 60 | 55 - 60 | ASTM D2240 |
| Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ASTM D4745-97 |
| Elongation at Break | >= 150 % | >= 150 % | ASTM D4745-97 |
| Coefficient of Friction, Static | 0.10 - 0.30 | 0.10 - 0.30 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 230 °C | 446 °F | DSC |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.0 @Frequency 60.0 - 2.00e+6 Hz |
2.0 @Frequency 60.0 - 2.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 - 40.0 kV/mm | 635 - 1020 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 65CI PC/ABS-Blend
- Proto3000 Objet Digital Materials™ DM_9610 Rubber-like Prototyping Polymer
- Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes
- Saint-Gobain CHR® M797 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- Vyncolit BXE650 Inorganic Filled Phenolic Molding Compound
- Tra-Con Tra-Bond 2106T Fast Cure Thixotropic Epoxy Adhesive
- Eurostar Starflam PW0042E PA6, 20% Mineral Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved