- Aclo Accutech Polypropylene Copolymer CP0437M40CL Mica Reinforced Coupled
Aclo Accutech Polypropylene Copolymer CP0437M40CL Mica Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437M40CL Mica Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | MD; ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 36 | 36 | ASTM D785 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ASTM D638 |
| Flexural Strength | 26.0 MPa | 3770 psi | ASTM D790 |
| Flexural Modulus | 3.800 GPa | 551.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C | 243 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C | 154 °F |
Users viewing this material also viewed the following:
- Polikim KESTLUB® Polyamide 6 + Lubricant
- Plastcom SLOVAMID 6 LI/1 LS PA6, improved strength, light stability
- Overview of materials for ABS/Polyester Alloy
- Kennametal Stellite Stellite® 21
- LATI Latamid 66 H2 G/25-V0HF1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- A. Schulman POLYBATCH™ Blue 4025 Concentrate Based In Polyethylene
- Eastman Ecdel PCCE 9967 Copolyester Ether Elastomer
- Dow 608A Low Density Polyethylene (LDPE)
- Dow FLEXOMER™ ETS-9064 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin
- Braskem PB682 Blow Molding Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved