Abatron AboCast 8110-8/AboCure 8110-1 Flexible Epoxy

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer	Abatron
Trade Name	AboCast
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast 8110-8/AboCure 8110-1 Flexible Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applications include: bonding, laminating, casting, embedding, electrical potting, impregnating, coating, etc. It can be supplied in several variations to modify viscosity, reaction rate, color, most physical and chemical properties, and with many fillers to meet most requirements.

Physical Properties	Metric	English	Comments
Water Absorption	5.8 % @Time 7200 sec	5.8 % @Time 2.00 hour	boil; cured 2 hours @ 93°C
Viscosity	2460 cP	2460 cP

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	70 @Temperature 75.0 °C	70 @Temperature 167 °F	cured 2 hrs. @ 93°C
Hardness, Shore D	60 @Temperature 25.0 °C	60 @Temperature 77.0 °F	cured 2 hrs. @ 93°C
	80 @Temperature 0.000 °C	80 @Temperature 32.0 °F	cured 2 hrs. @ 93°C
	86 @Temperature -60.0 °C	86 @Temperature -76.0 °F	cured 2 hrs. @ 93°C
Tensile Strength, Ultimate	1.48 MPa	215 psi	cured 2 hours @ 93°C
	9.963 MPa	1445 psi	cured 8 hours @ 93°C
Elongation at Break	62 %	62 %	cured 8 hours @ 93°C
	117 %	117 %	cured 2 hours @ 93°C
Shear Strength	6.69 MPa @Temperature 75.0 °C	970 psi @Temperature 167 °F	Tensile, Al/Al lap joint; cured 2 hours @ 93°C
	15.7 MPa @Temperature 25.0 °C	2280 psi @Temperature 77.0 °F	Tensile, Al/Al lap joint; cured 2 hours @ 93°C
	27.4 MPa @Temperature 0.000 °C	3980 psi @Temperature 32.0 °F	Tensile, Al/Al lap joint; cured 2 hours @ 93°C

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.40e+7 ohm-cm @Temperature 150 °C	3.40e+7 ohm-cm @Temperature 302 °F	cured 2 hours @ 93°C
	6.60e+7 ohm-cm @Temperature 100 °C	6.60e+7 ohm-cm @Temperature 212 °F	cured 2 hours @ 93°C
	7.40e+7 ohm-cm @Temperature 112 °C	7.40e+7 ohm-cm @Temperature 234 °F	cured 2 hours @ 93°C
	1.50e+11 ohm-cm @Temperature 25.0 °C	1.50e+11 ohm-cm @Temperature 77.0 °F	cured 2 hours @ 93°C

Processing Properties	Metric	English	Comments
Pot Life	52 min @Temperature 25.0 °C	52 min @Temperature 77.0 °F	200 g
Gel Time	13.0 min @Temperature 93.0 °C	13.0 min @Temperature 199 °F	10 g

Descriptive Properties	Value	Comments
Parts by Weight (pbw)	100	AboCast 8110-8
	7.4	AboCure 8110-1