Abatron AboCast 8110-2/AboCure 8110-1 Flexible Epoxy

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer	Abatron
Trade Name	AboCast
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast 8110-2/AboCure 8110-1 Flexible Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applications include: bonding, laminating, casting, embedding, electrical potting, impregnating, coating, etc. It can be supplied in several variations to modify viscosity, reaction rate, color, most physical and chemical properties, and with many fillers to meet most requirements.

Physical Properties	Metric	English	Comments
Water Absorption	4.5 % @Time 2.59e+6 sec	4.5 % @Time 720 hour	immersion; cured 30 days @ 25°C
	4.9 % @Time 2.59e+6 sec	4.9 % @Time 720 hour	immersion; cured 7 days @ 25°C
Viscosity	1600 cP	1600 cP

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	37 @Temperature 75.0 °C	37 @Temperature 167 °F	cured 7 days @ 25°C
	58 @Temperature 75.0 °C	58 @Temperature 167 °F	cured 30 days @ 25°C
	75 @Temperature 25.0 °C	75 @Temperature 77.0 °F	cured 7 days @ 25°C
	85 @Temperature 25.0 °C	85 @Temperature 77.0 °F	cured 30 days @ 25°C
	89 @Temperature -60.0 °C	89 @Temperature -76.0 °F	cured 30 days @ 25°C
	89 @Temperature -60.0 °C	89 @Temperature -76.0 °F	cured 7 days @ 25°C
Tensile Strength, Ultimate	16.3 MPa	2360 psi	cured 7 days @ 25°C
	37.9 MPa	5500 psi	cured 30 days @ 25°C
Elongation at Break	39 %	39 %	cured 30 days @ 25°C
	70 %	70 %	cured 7 days @ 25°C
Shear Strength	2.34 MPa @Temperature 75.0 °C	340 psi @Temperature 167 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C
	22.2 MPa @Temperature 25.0 °C	3220 psi @Temperature 77.0 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C
	30.8 MPa @Temperature 0.000 °C	4470 psi @Temperature 32.0 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C

Electrical Properties	Metric	English	Comments
Volume Resistivity	6.20e+7 ohm-cm @Temperature 100 °C	6.20e+7 ohm-cm @Temperature 212 °F	cured 30 days @ 25°C
	7.20e+8 ohm-cm @Temperature 100 °C	7.20e+8 ohm-cm @Temperature 212 °F	cured 7 days @ 25°C
	3.00e+12 ohm-cm @Temperature 25.0 °C	3.00e+12 ohm-cm @Temperature 77.0 °F	cured 7 days @ 25°C
	4.90e+13 ohm-cm @Temperature 25.0 °C	4.90e+13 ohm-cm @Temperature 77.0 °F	cured 30 days @ 25°C

Processing Properties	Metric	English	Comments
Pot Life	30 min @Temperature 25.0 °C	30 min @Temperature 77.0 °F	200 g

Descriptive Properties	Value	Comments
Parts by Weight (pbw)	100	AboCast 8110-2
	9.7	AboCure 8110-1