Aaron Industries AAROPRENE® GFPP 2030 Glass Filled Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Aaron Industries Corporation |
| Trade Name | AAROPRENE® GFPP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aaron Industries AAROPRENE® GFPP 2030 Glass Filled Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AAROPRENE® GFPP 2000 Series Glass Reinforced CompoundsMelt flow index may be specified. Color may be specified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | Glass; ASTM D2584 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 51.0 MPa | 7400 psi | ASTM D638 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Michelman® DigiGuard® Gloss 100 Water based overprint varnish
- Lavergne VYPET VNT 335 PET 35% Glass - Mineral Reinforced
- Eastman Tenite 360E3V45512 Propionate Water Clear, Trsp
- ExxonMobil 627 Mobilgear 600 Series
- ConocoPhillips El Mar® Grade 15W-40 Mid Ash Supreme Oil
- Akzo Nobel Expancel® 820 WU 40 Wet unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved