- Aaron Industries AAROPRENE® AEPC 5000-2 Engineered Polycarbonate Resin
Aaron Industries AAROPRENE® AEPC 5000-2 Engineered Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Aaron Industries Corporation |
| Trade Name | AAROPRENE® AEPC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aaron Industries AAROPRENE® AEPC 5000-2 Engineered Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt flow index may be specified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 61.4 MPa | 8900 psi | ASTM D638 |
| Flexural Modulus | 2.38 GPa | 345 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 104 PC (Europe-Africa-Middle East)
- LNP ULTEM® EXCP0096 Polyetherimide, 30% Carbon Fiber Reinforcement, 10% PTFE Lubricant (discontinued **)
- Lehmann & Voss LUVOCOM® 1-RG 2 Polyamide 66, with carbon fiber, heat stabilized
- Kuraray Genestarâ„¢ TA104 Nylon
- Hexcel® HexWeb® HRP - 3/8 - 3.5 Fiberglass/Phenolic Honeycomb
- Dow Corning SE 4486 SILICONE RTV
- Denka TP-802 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
- Bulk Molding Compounds BMC 1454 for Injection Molding Circuit Breakers
- Arlon R37503G015 0.015" (0.381 mm) Cured Fluorosilicone Rubber
Copyright © lookpolymers.com All Rights Reserved