ATI Allvac® Vasco® 13-8Mo Precipitation Hardening Steel, Heat Treatment: 927°C (1700°F) + Age
| Category | Metal , Ferrous Metal , Stainless Steel , Precipitation Hardening Stainless |
| Manufacturer | ATI Allvac |
| Trade Name | Vasco® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allvac® Vasco® 13-8Mo Precipitation Hardening Steel, Heat Treatment: 927°C (1700°F) + Age.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Allvac.Applications: Airframe structurals, missile components, valve parts, fasteners, chemical process equipment.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.72 g/cc | 0.279 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 411 | 411 | Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball |
| Hardness, Knoop | 450 | 450 | Estimated from Rockwell C value. |
| Hardness, Rockwell C | 44 | 44 | |
| Hardness, Vickers | 430 | 430 | Estimated from Rockwell C value. |
| Tensile Strength, Ultimate | 1483 MPa | 215100 psi | |
| Tensile Strength, Yield | 1379 MPa @Strain 0.200 % |
200000 psi @Strain 0.200 % |
|
| Elongation at Break | >= 10 % | >= 10 % | |
| Reduction of Area | >= 40 % | >= 40 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 1.05 % | 1.05 % | |
| Carbon, C | 0.050 % | 0.050 % | |
| Chromium, Cr | 12.8 % | 12.8 % | |
| Iron, Fe | 76 % | 76 % | as balance |
| Manganese, Mn | 0.10 % | 0.10 % | |
| Molybdenum, Mo | 2.3 % | 2.3 % | |
| Nickel, Ni | 8.0 % | 8.0 % | |
| Nitrogen, N | 0.0050 % | 0.0050 % | |
| Phosphorous, P | 0.0050 % | 0.0050 % | |
| Silicon, Si | 0.050 % | 0.050 % | |
| Sulfur, S | 0.0040 % | 0.0040 % |
Users viewing this material also viewed the following:
- Michelman® HydraBan® 708 Water resistant paper coating
- Silberline Extra Fine "T"
- UBE UBESTA® 3030U Nylon 12 (After Fuel C for 1000 hours)
- Plenco 00732 Melamine-Phenolic, Granular, Compression Molded
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.25 PHR Zinc Stearate
- Arlon 51366X015 0.016" (0.406 mm) Uncured Silicone Rubber with Fiberglass Substrate
- BASF Novolen® 1040 N Polypropylene
- Quadrant EPP Duratron® PAI T4301 Polyamide-imide, extruded bearing grade (ASTM Product Data Sheet)
- SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved