ALM PA-640-GSL Filled Nylon 12 Prototyping Polymer

Category	Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	ALM Advanced Laser Materials
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ALM PA-640-GSL Filled Nylon 12 Prototyping Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This carbon fiber/glass sphere filled composite is an easy to process, extremely light weight filled PA 12 material.Improved dimensional stability, recyclability, and increased stiffness.Good Z direction properties and an excellent choice for applications requiring reduced weight and higher temperatures.Information provided by Advanced Laser Materials (ALM).

Physical Properties	Metric	English	Comments
Bulk Density	0.370 g/cc	0.0134 lb/in³	ASTM D1895
Density	0.820 g/cc	0.0296 lb/in³	Sintered; ASTM D792
Particle Size	55 µm	55 µm	D50
	35 - 100 µm	35 - 100 µm	D10-D90
Melt Flow	26 g/10 min @Load 5.00 kg, Temperature 235 °C	26 g/10 min @Load 11.0 lb, Temperature 455 °F	3 min; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	33.0 MPa	4790 psi	Z; ASTM D638
	49.0 MPa	7110 psi	XY; ASTM D638
Elongation at Break	3.0 %	3.0 %	XY; ASTM D638
	3.0 %	3.0 %	Z; ASTM D638
Tensile Modulus	1.945 GPa	282.1 ksi	Z; ASTM D638
	3.816 GPa	553.5 ksi	XY; ASTM D638
Flexural Modulus	4.313 GPa	625.5 ksi	Z; ASTM D790
	5.04 GPa	731 ksi	XY; ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	184 °C	363 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	180 °C	356 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	170 °C	338 °F	ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	760000 ohm-cm	760000 ohm-cm	ASTM D257
Surface Resistance	40000 ohm	40000 ohm