A. Schulman ComAlloy Lubrilon® 511 Polycarbonate, Glass Fiber/PTFE, UL

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass + PTFE Filled
Manufacturer	A. Schulman ComAlloy
Trade Name	Lubrilon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman ComAlloy Lubrilon® 511 Polycarbonate, Glass Fiber/PTFE, UL.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.

Physical Properties	Metric	English	Comments
Density	1.29 g/cc	0.0466 lb/in³
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength, Ultimate	76.0 MPa	11000 psi	ASTM D638
Elongation at Break	10 %	10 %	ASTM D638
Flexural Strength	127 MPa	18400 psi	ASTM D790
Flexural Modulus	4.10 GPa	595 ksi	ASTM D790
Izod Impact, Notched	0.480 J/cm	0.899 ft-lb/in	ASTM D256
Izod Impact, Unnotched	2.67 J/cm	5.00 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	141 °C	286 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	133 °C	271 °F	ASTM D648
Glass Transition Temp, Tg	145 - 150 °C	293 - 302 °F

Processing Properties	Metric	English	Comments
Middle Barrel Temperature	304 - 321 °C	579 - 610 °F