3M Scotch-Weld™ TE200 Polyurethane Reactive Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ TE200 Polyurethane Reactive Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Extrudable grade with fast set time, long open time ideal for bonding wood. Yields thin glue lines.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³
Brookfield Viscosity	3000 cP	3000 cP	Thermosel using spindle #27

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60
Tensile Strength at Break	27.6 MPa	4000 psi	ASTM D638 Die C
Elongation at Break	625 %	625 %	ASTM D638 Die C
Tensile Modulus	0.0669 GPa	9.70 ksi	ASMT D638 Die C
Shear Strength	4.27 MPa @Temperature 82.0 °C	620 psi @Temperature 180 °F	Overlap, Maple
	4.48 MPa @Temperature 23.0 °C	650 psi @Temperature 73.4 °F	Overlap, Polystyrene, Substrate Failure
	8.62 MPa @Temperature 23.0 °C	1250 psi @Temperature 73.4 °F	Overlap, Polyacrylic, Substrate Failure
	8.62 MPa @Temperature 23.0 °C	1250 psi @Temperature 73.4 °F	Overlap, ABS, Substrate Failure
	10.7 MPa @Temperature 82.0 °C	1550 psi @Temperature 180 °F	Overlap, FRP
	11.7 MPa @Temperature 23.0 °C	1700 psi @Temperature 73.4 °F	Overlap, FRP, Substrate Failure
	13.4 MPa @Temperature 23.0 °C	1950 psi @Temperature 73.4 °F	Overlap, Maple
	14.8 MPa @Temperature 23.0 °C	2150 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
	15.2 MPa @Temperature 23.0 °C	2200 psi @Temperature 73.4 °F	Overlap, Polycarbonate, Substrate Failure
Peel Strength	1.58 kN/m	9.00 pli	180°, Polystyrene
	2.10 kN/m	12.0 pli	T-Peel, Initial
	5.43 kN/m	31.0 pli	T-Peel, Aged 71°C for 2 weeks, Substrate failure
	8.06 kN/m	46.0 pli	180°, Polyacrylic, Cotton duck failed during testing
	14.0 kN/m	80.0 pli	180°, FRP, Cotton duck failed during testing
	14.0 kN/m	80.0 pli	180°, ABS, Cotton duck failed during testing
	14.0 kN/m	80.0 pli	180°, PVC, Cotton duck failed during testing
	15.8 kN/m	90.0 pli	180°, Polycarbonate, Cotton duck failed during testing

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F

Processing Properties	Metric	English	Comments
Cure Time	2.00 min	0.0333 hour	Set Time

Descriptive Properties	Value	Comments
Appearance	White/Off-White