3M Scotch-Weld™ TE100 Polyurethane Reactive Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ TE100 Polyurethane Reactive Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Extrudable grade with medium set time and low viscosity ideal for bonding wood. Bonds selected plastics. Yields thin glue lines.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³
Brookfield Viscosity	7000 cP	7000 cP	Thermosel using spindle #27

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	61	61
Tensile Strength at Break	29.0 MPa	4210 psi	ASTM D638 Die C
Elongation at Break	675 %	675 %	ASTM D638 Die C
Tensile Modulus	0.0841 GPa	12.2 ksi	ASMT D638 Die C
Shear Strength	1.38 MPa @Temperature 23.0 °C	200 psi @Temperature 73.4 °F	Overlap, Polystyrene
	2.62 MPa @Temperature 82.0 °C	380 psi @Temperature 180 °F	Overlap, Maple
	5.58 MPa @Temperature 82.0 °C	810 psi @Temperature 180 °F	Overlap, FRP
	6.34 MPa @Temperature 23.0 °C	920 psi @Temperature 73.4 °F	Overlap, ABS, Substrate Failure
	7.93 MPa @Temperature 23.0 °C	1150 psi @Temperature 73.4 °F	Overlap, Polyacrylic, Substrate Failure
	13.2 MPa @Temperature 23.0 °C	1910 psi @Temperature 73.4 °F	Overlap, Maple
	13.9 MPa @Temperature 23.0 °C	2010 psi @Temperature 73.4 °F	Overlap, Polycarbonate
	14.5 MPa @Temperature 23.0 °C	2100 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
	17.6 MPa @Temperature 23.0 °C	2550 psi @Temperature 73.4 °F	Overlap, FRP
Peel Strength	2.10 kN/m	12.0 pli	T-Peel, Initial, Substrate failure
	3.86 kN/m	22.0 pli	T-Peel, Aged 71°C for 2 weeks, Substrate failure
	5.08 kN/m	29.0 pli	180°, Polyacrylic
	12.3 kN/m	70.0 pli	180°, ABS, Cotton duck failed during testing
	12.3 kN/m	70.0 pli	180°, PVC, Cotton duck failed during testing
	13.5 kN/m	77.0 pli	180°, Polycarbonate, Cotton duck failed during testing
	14.2 kN/m	81.0 pli	180°, FRP, Cotton duck failed during testing

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F

Processing Properties	Metric	English	Comments
Cure Time	1.00 min	0.0167 hour	Set Time

Descriptive Properties	Value	Comments
Appearance	White/Off-White