3M Scotch-Weld™ Medium Instant Wood Adhesives and Surface Activator

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ Medium Instant Wood Adhesives and Surface Activator.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in the manufacture and repair of furniture, cabinets, and other wood products.Information provided by 3M

Physical Properties	Metric	English	Comments
Viscosity	>= 450 cP	>= 450 cP

Mechanical Properties	Metric	English	Comments
Shear Strength	2.07 MPa	300 psi	Overlap, Particleboard, Substrate Failure
	2.76 MPa	400 psi	Overlap, Melamine, Substrate Failure
	3.10 MPa	450 psi	Overlap, Pine, Substrate/Cohesive Failure
	3.10 MPa	450 psi	Overlap, MDF, Cohesive Failure
	3.45 MPa	500 psi	Overlap, Polyurethane Finish, Adhesive Failure
	4.14 MPa	600 psi	Overlap, Polyacrylic Finish, Cohesive Failure
	6.21 MPa	900 psi	Overlap, Poplar, Substrate/Cohesive Failure
	6.21 MPa	900 psi	Overlap, High Pressure Laminate, Substrate Failure
	6.89 MPa	1000 psi	Overlap, Plywood, Cohesive Failure
	7.24 MPa	1050 psi	Overlap, Maple, Substrate Failure
	13.4 MPa	1950 psi	Overlap, Aluminum, Adhesive Failure
	16.2 MPa	2350 psi	Overlap, Oak, Substrate/Cohesive Failure
	19.7 MPa	2850 psi	Overlap, Steel, Adhesive Failure
	3.10 MPa @Temperature 32.0 °C	450 psi @Temperature 89.6 °F	Overlap, Aluminum, 90% RH, Adhesive Failure
	3.79 MPa @Temperature 32.0 °C	550 psi @Temperature 89.6 °F	Overlap, Polyurethane Finish, 90% RH, Adhesive Failure
	4.14 MPa @Temperature 32.0 °C	600 psi @Temperature 89.6 °F	Overlap, Pine, 90% RH, Adhesive Failure
	6.55 MPa @Temperature 32.0 °C	950 psi @Temperature 89.6 °F	Overlap, Plywood, 90% RH, Substrate Failure
	6.89 MPa @Temperature 66.0 °C	1000 psi @Temperature 151 °F	Overlap, Polyurethane Finish, Adhesive Failure
	7.24 MPa @Temperature 66.0 °C	1050 psi @Temperature 151 °F	Overlap, Plywood, Substrate Failure
	7.24 MPa @Temperature 66.0 °C	1050 psi @Temperature 151 °F	Overlap, Aluminum, Adhesive Failure
	7.58 MPa @Temperature 66.0 °C	1100 psi @Temperature 151 °F	Overlap, Pine, Adhesive Failure
	12.8 MPa @Temperature 66.0 °C	1850 psi @Temperature 151 °F	Overlap, Oak, Substrate/Adhesive Failure
	13.4 MPa @Temperature 32.0 °C	1950 psi @Temperature 89.6 °F	Overlap, Oak, 90% RH, Substrate/Adhesive Failure

Processing Properties	Metric	English	Comments
Cure Time	1440 min	24.0 hour	Full Cure

Descriptive Properties	Value	Comments
Appearance	Clear-Slightly yellow liquid