3M Scotch-Weld™ CA4 Instant Adhesive
| Category | Polymer , Adhesive |
| Manufacturer | 3M |
| Trade Name | Scotch-Weld™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Scotch-Weld™ CA4 Instant Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Fast setting for a variety of plastics and rubbers.Information provided by 3M
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Viscosity | 150 cP | 150 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Shear Strength | 0.241 MPa | 35.0 psi | Overlap, Nitrile Rubber; ASTM D1002-64 |
| 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 | |
| 5.52 MPa | 800 psi | Overlap, ABS; ASTM D1002-64 | |
| 5.52 MPa | 800 psi | Overlap, Rigid PVC; ASTM D1002-64 | |
| 15.9 MPa | 2300 psi | Overlap, Steel; ASTM D1002-64 | |
| 19.3 MPa | 2800 psi | Overlap, Aluminum; ASTM D1002-64 | |
| Peel Strength | 0.175 - 0.351 kN/m | 1.00 - 2.00 pli | T-Peel; ASTM D1876-61T |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 0.083333 - 0.666666 min | 0.0013889 - 0.0111111 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear |
Users viewing this material also viewed the following:
- LG Chemical HI100 ABS, High Impact
- Momentive Performance Materials HBR Hot-Pressed Boron Nitride
- Techmer ES Electrafil® J-1305/CF/30/TF/15 NAT PPS
- Sharadaa Ceramics Sharada RFC-Fused Silica Gel Bonded Castables
- Teknor Apex APEX® 3210-55 Polyvinyl Chloride, Flexible
- Samsung Cheil Industries Starex® VE-0812 ABS, Unreinforced FR
- Eagle Brass 521 Phosphor Bronzes 8% C, 1/4 Hard
- BASF Elastoblend LP 9192 TPUR
- Solvay TECHNYL® A 31T1 MZ40 PA66, 40% mineral fiber, DRY
Copyright © lookpolymers.com All Rights Reserved