3M Dyneon™ FC 2170 Fluoroelastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Rubber or Thermoset Elastomer (TSE)
Manufacturer 3M Dyneon™
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ FC 2170 Fluoroelastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Dyneon™ Fluoroelastomer FC 2170 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formulations. The “dry” ingredients should be blended before adding to the masticated gum. For best results, Dyneon FC 2170 should be banded on the mill several minutes prior to adding the blended dry ingredients. Once mixed, the compounded stocks have good scorch resistance and storage stabilityComposition: di-polymer of vinylidene fluoride and hexafluoropropyleneProcess targets: compression moldingProprietary incorporated cure technologyHigher viscosity version of FC 2120Information provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Specific Gravity 1.80 g/cc
1.80 g/cc
Mooney Viscosity 31

@Temperature 121 °C
31

@Temperature 250 °F
ML1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 75
75
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240
Tensile Strength at Break 14.8 MPa
2150 psi
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
Elongation at Break 190 %
190 %
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
100% Modulus 0.00603 GPa
0.875 ksi
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
Compression Set 16 %
16 %
Aged 70 hours @ 200°C, -214 O-rings; ASTM D395 Method B
Thermal Properties Metric English Comments
Transformation Temperature -18.0 °C
-0.400 °F
TR10; ASTM D1329
Component Elements Properties Metric English Comments
Fluorine, F 65.9 %
65.9 %
Descriptive Properties Value Comments
Color Opaque Off-White
MH, Maximum Torque 23.2 inch-lb
100 cpm, 0.5° Arc, 6 Minutes
ML, Minimum Torque @ 177°C 1.1 inch-lb
100 cpm, 0.5° Arc, 6 Minutes
Solubility Ketones and Esters
t`50, Time to 50% cure 2.2 Minutes
100 cpm, 0.5° Arc, 6 Minutes
t`90 - Time to 90% cure 3.1 Minutes
100 cpm, 0.5° Arc, 6 Minutes
ts2 - Time to 2 in-lb rise from min 1.8 Minutes
100 cpm, 0.5° Arc, 6 Minutes