3M Dyneon™ CCM605 PTFE, 25% Glass Filled (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ CCM605 PTFE, 25% Glass Filled (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Type II, free flowing.Typical Applications: Finished or semi-finished parts: sheets, rods, tubes, billets for skiving of films or machining into complex shapes.Information provided by the Dyneon division of 3M.

Physical Properties	Metric	English	Comments
Specific Gravity	2.24 g/cc	2.24 g/cc	ASTM D4894
Bulk Density	0.710 g/cc	0.0257 lb/in³	ASTM D4894
Particle Size	750 µm	750 µm	ASTM D4894
Deformation	1.0 % @Pressure 15.00 MPa	1.0 % @Pressure 2175 psi	permanent; ASTM D621
	2.0 % @Time 86400 sec, Pressure 15.00 MPa	2.0 % @Time 24.0 hour, Pressure 2175 psi	ASTM D621

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	62	62	Initial; ASTM D2240
	57 @Time 15.0 sec	57 @Time 0.00417 hour	ASTM D2240
Tensile Strength at Break	15.2 MPa	2200 psi	ASTM D4894
Elongation at Break	300 %	300 %	ASTM D4894
Tensile Modulus	0.165 GPa	24.0 ksi	ASTM D638

Thermal Properties	Metric	English	Comments
CTE, linear	73.8 µm/m-°C @Temperature 30.0 - 100 °C	41.0 µin/in-°F @Temperature 86.0 - 212 °F	ASTM E831
	91.8 µm/m-°C @Temperature 100 - 200 °C	51.0 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
	140 µm/m-°C @Temperature 200 - 300 °C	78.0 µin/in-°F @Temperature 392 - 572 °F	ASTM E831
Thermal Conductivity	0.240 W/m-K @Temperature 100 °C	1.67 BTU-in/hr-ft²-°F @Temperature 212 °F	ASTM E1530
	0.260 W/m-K @Temperature 250 °C	1.80 BTU-in/hr-ft²-°F @Temperature 482 °F	ASTM E1530
Shrinkage	2.8 %	2.8 %	ASTM D4894