- 3M Dyneon™ CC698 PTFE 20% Fiberglass/Carbon Filled (discontinued **)
3M Dyneon™ CC698 PTFE 20% Fiberglass/Carbon Filled (discontinued **)
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Dyneon™ CC698 PTFE 20% Fiberglass/Carbon Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Form: Black, pelletized powder. Applications include valve seats.Data provided by Dyneon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.18 g/cc | 0.0788 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | value after 15 sec; ASTM D2240 |
| 66 | 66 | initial value; ASTM D2240 | |
| Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D4745 |
| Elongation at Break | 150 % | 150 % | ASTM D4894 |
| Flexural Yield Strength | <= 31.0 MPa | <= 4500 psi | ASTM D790 |
| Compressive Yield Strength | 10.8 MPa | 1570 psi | ASTM D695 |
| Compressive Modulus | 0.570 GPa | 82.7 ksi | ASTM D695 |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | ASTM D3702 |
| Coefficient of Friction, Static | 0.23 | 0.23 | ASTM D3702 |
| K (wear) Factor | 18.5 x 10-8 mm³/N-M | 9.20 x 10-10 in³-min/ft-lb-hr | at 5000 psi - fpm PV; ASTM D3702 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 162 µm/m-°C @Temperature 20.0 °C |
90.0 µin/in-°F @Temperature 68.0 °F |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL L6303 Conductive Elastomer
- Overview of materials for High Density Polyethylene (HDPE), Copolymer Film Grade
- Lanxess Durethan® BKV 30 EF 000000 Nylon 6, 30% Glass Fiber
- SABIC Innovative Plastics ULTEM HU2310 PEI
- Teknor Apex APEX® 80457 Polyvinyl Chloride, Flexible
- Arlon P31000N010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Arlon T3030-R004 0.030" (0.762 mm) Thick, 1" wide, Cured Fusible Silicone Rubber with Sinusoidal Fiberglass Substrate
- ExxonMobil Santoprene® 123-50 Thermoplastic Elastomer (discontinued **)
- ChevronTexaco Havoline® SAE 10W-30 Synthetic Motor Oil
Copyright © lookpolymers.com All Rights Reserved