Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 3.00e+11 ohm-cm | 3.00e+11 ohm-cm | ASTM D257-99 |
Rogers Corporation Poron® 4701-30-25 Urethane Foam, Very Soft Very soft, easily compressed for use where flexibility is a key requirement. Standard available thickness range from 0.021"Features and Benefits of PORON Products: Excellent compression set resi.. |
|||
Volume Resistivity | >= 3.00e+11 ohm-cm @Temperature 20.0 °C |
>= 3.00e+11 ohm-cm @Temperature 68.0 °F |
|
Sibur NGP 30-32 Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p.. |
|||
Volume Resistivity | >= 3.00e+11 ohm-cm @Temperature 20.0 °C |
>= 3.00e+11 ohm-cm @Temperature 68.0 °F |
|
Sibur NGP 40-32 Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p.. |
|||
Volume Resistivity | 3.00e+11 ohm-cm | 3.00e+11 ohm-cm | ASTM D257 |
Teknor Apex APEX® 586 Polyvinyl Chloride, Flexible Notes: 60°C Insulation; RoHS Compliant Uses: Tubing; Wire JacketingForms: Pellets Wire Types: SPT-1; SPT-2 Agency Ratings: UL 498; UL 62 Processing Method: Injection Molding Additional Informatio.. |
|||
Volume Resistivity | 3.00e+11 ohm-cm | 3.00e+11 ohm-cm | ASTM D247 |
Plenco 4504 Phenolic, Granular, Injection Molded Plenco 04504 is a renumber of Plaslok 504. Plenco 04504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding c.. |
|||
Volume Resistivity | 3.00e+11 ohm-cm | 3.00e+11 ohm-cm | |
Reliance Industries PVAXX H60 The key property of all PVAXX polymer is this product`s unique capacity to biodegrade into non-toxic residues under both aerobic and non-aerobic conditions.Information provided by Reliance Industrie.. |