Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0001278 ohm-cm @Temperature 1100 °C |
0.0001278 ohm-cm @Temperature 2010 °F |
|
Haynes HR-120® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Electrical Resistivity | 0.0001278 ohm-cm @Temperature 1100 °C |
0.0001278 ohm-cm @Temperature 2010 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Electrical Resistivity | 0.0001278 ohm-cm @Temperature 1100 °C |
0.0001278 ohm-cm @Temperature 2010 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Electrical Resistivity | 0.0001278 ohm-cm @Temperature 1100 °C |
0.0001278 ohm-cm @Temperature 2010 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Electrical Resistivity | 0.0001278 ohm-cm @Temperature 1100 °C |
0.0001278 ohm-cm @Temperature 2010 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Electrical Resistivity | 0.0001278 ohm-cm @Temperature 1100 °C |
0.0001278 ohm-cm @Temperature 2010 °F |
|
Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Electrical Resistivity | 0.0001278 ohm-cm | 0.0001278 ohm-cm | |
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |