Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 1.30 J/g-°C @Temperature 60.0 °C |
0.311 BTU/lb-°F @Temperature 140 °F |
DSC |
Eastman Eastar GN002 Copolyester, Natural
(discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 60.0 °C |
0.311 BTU/lb-°F @Temperature 140 °F |
DSC |
Eastman Eastar GN005 Copolyester, Natural
(discontinued **) Eastar GN005 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN005 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 60.0 °C |
0.311 BTU/lb-°F @Temperature 140 °F |
|
Eastman EASTALLOY Polymer DA003-8999K, Clear Alloy
(discontinued **) Properties below based on a film thickness of 250 microns. CO2 Permeability is 49 cm3·mm/m2·24h·atm per ASTM D 1434.Product Description: EASTALLOY DA003-8999K Polymer is a clear copolyester/pol.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 50.0 °C |
0.311 BTU/lb-°F @Temperature 122 °F |
DSC |
Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable gra.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 50.0 °C |
0.311 BTU/lb-°F @Temperature 122 °F |
DSC |
Solvay Specialty Polymers KetaSpire® KT-820 GF30 Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 60.0 °C |
0.311 BTU/lb-°F @Temperature 140 °F |
|
Eastman Drystar 0113 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 60.0 °C |
0.311 BTU/lb-°F @Temperature 140 °F |
DSC |
Eastman Drystar 0601 Copolyester, Injection Molded This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 60.0 °C |
0.311 BTU/lb-°F @Temperature 140 °F |
DSC |
Eastman Eastman 1223 Copolyester Applications:Blown filmCredit cardsDebit cardsDeodorant packagingElectronic packagingFabricated boxesFlexible packagingFood packagingFurniture/Furniture trimGaming cardsGift cardsIdentification card.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 250 °C |
0.311 BTU/lb-°F @Temperature 482 °F |
|
Carlisle 201HD Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 250 °C |
0.311 BTU/lb-°F @Temperature 482 °F |
|
Carlisle 201LL Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 250 °C |
0.311 BTU/lb-°F @Temperature 482 °F |
|
Carlisle 201HL Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t.. |
|||
Specific Heat Capacity | 1.30 J/g-°C @Temperature 250 °C |
0.311 BTU/lb-°F @Temperature 482 °F |
|
Carlisle 201LD Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t.. |