Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.406 J/g-°C @Temperature 0.000 °C |
0.0970 BTU/lb-°F @Temperature 32.0 °F |
|
Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 0.000 °C |
0.0970 BTU/lb-°F @Temperature 32.0 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 200 °C |
0.0970 BTU/lb-°F @Temperature 392 °F |
|
HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked Solution Treated, 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 200 °C |
0.0970 BTU/lb-°F @Temperature 392 °F |
|
HP Alloys Alloy B-2, Solution Treated, 20% Cold Worked Solution Treated, 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 200 °C |
0.0970 BTU/lb-°F @Temperature 392 °F |
|
HP Alloys Alloy B-2, Solution Treated, 30% Cold Worked Solution Treated, 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 200 °C |
0.0970 BTU/lb-°F @Temperature 392 °F |
|
HP Alloys Alloy B-2, Solution Treated, 40% Cold Worked Solution Treated, 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 0.000 °C |
0.0970 BTU/lb-°F @Temperature 32.0 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 0.000 °C |
0.0970 BTU/lb-°F @Temperature 32.0 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Specific Heat Capacity | 0.406 J/g-°C @Temperature 200 °C |
0.0970 BTU/lb-°F @Temperature 392 °F |
|
HP Alloys Alloy B-2, Solution Treated, 50% Cold Worked Solution Treated, 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |