Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, GTAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 199 °C |
129 BTU-in/hr-ft²-°F @Temperature 390 °F |
|
EDRO UltraChem® #15 Precipitation Hardening Stainless Mold Steel Ultrachem® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by: exceptional corrosion resistance, uniform hardness in all dimensions, .. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 199 °C |
129 BTU-in/hr-ft²-°F @Temperature 390 °F |
|
EDRO UltraChem® ESR #16 Precipitation Hardening Stainless Mold Steel Ultrachem ESR® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by exceptional polishability, exceptional corrosion resistance, unifor.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Carpenter Gall-Tough® Stainless Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 400 °C |
129 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 18.6 W/m-K @Temperature 500 °C |
129 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |