Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Multimet® alloy, GTAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 593 °C |
139 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 593 °C |
139 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 20.0 °C |
139 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
hardened to 62 HRC |
Bohler-Uddeholm AISI D2 Cold Work Tool Steel AISI D2 is a high-carbon, high-chromium tool steel alloyed with molybdenum and vanadiumAISI AD2 is characterized by: High wear resistance High compressive strength Good through-hardening properties.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |