Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C. (dry sample) |
Omnia Plastica Akulon® PA 66 - Akulon 66 - at 50% RH Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C. |
Omnia Plastica Akulon® PA 66 - Akulon 66 - Dry Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Continuous (GTP 50% Tensile); IEC 60216 |
PolyOne Bergamid™ B650 G/Mi20 UF Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Continuous (GTP 50% Tensile); IEC 60216 |
PolyOne Bergamid™ B650 Mi10 Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Abatron 440 A/B Filled Potting Compound
(discontinued **) Black or color dielectric hard casting adhesive room temperature epoxy. 100/20 ratio.Information provided by Abatron. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Abatron 440 GRA5 A/B Filled Potting Compound
(discontinued **) Gray dielectric hard casting adhesive room temperature epoxy. 100/20 ratio.Information provided by Abatron. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Abatron 810330 A/B Filled Potting Compound
(discontinued **) Filled casting, potting, and adhesive. Flexible arc track resistant. 100/18.5 ratio.Information provided by Abatron. |
|||
Maximum Service Temperature, Air | 95.0 - 105 °C | 203 - 221 °F | Softening point |
Mitsui MILEXâ„¢ RN-2830MB Acrylic Rubber Modified Phenolic Resin The MILEXâ„¢ Family of products is widely featured in brake systems of automobiles made by automakers through Mitsui Chemicals'. The phenolic material is primarily used as binders in brake pad.. |
|||
Maximum Service Temperature, Air | 95.0 - 105 °C | 203 - 221 °F | Softening point |
Mitsui MILEXâ„¢ RN-2830MR Acrylic Rubber Modified Phenolic Resin The MILEXâ„¢ Family of products is widely featured in brake systems of automobiles made by automakers through Mitsui Chemicals'. The phenolic material is primarily used as binders in brake pad.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | 5000 hours; 50% Tensile Strength; IEC 216; DIN 53446 |
Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oil.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | 5000 hours; 50% Tensile Strength; IEC 216; DIN 53446 |
Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oil.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Goodfellow Polyhydroxybutyrate - Biopolymer PHB PHB and its copolymers with polyhydroxyvalerate (PHV) are melt-processable semi-crystalline thermoplastics made by biological fermentation from renewable carbohydrate feedstocks. They have been desc.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Heat Distortion, Annealed; ASTM D648 |
Total PSI 740 Polystyrene Polystyrene 740 is an impact polystyrene designed for extrusion and injection molding. It is especially suitable for extrusion thermoforming applications requiring high glass and high stiffness, suc.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Zotefoams Plastazote® LD30SD Static Dissipative Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Zotefoams Plastazote® LD32CN Conductive Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Zotefoams Plastazote® MP15FR Metallocene Polyethylene Foam, Flame Retardant Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
Zotefoams Plastazote® MP24 Metallocene Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Wet Service |
Chesterton ARC BX1 Sliding Wear Compound Description: An advanced contractor grade ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Wet Service |
Chesterton ARC MX1 Vertical Build Extreme Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It is applied at a thickness of 6 mm (1/4”).. |
|||
Maximum Service Temperature, Air | <= 95.0 °C | <= 203 °F | Laundering Resistance |
EMS-Griltech Griltex® 2A Copolyamide Hotmelt Adhesive (Apparel Interlinings) Description: GRILTEX adhesive products, either in pellet or powdered form, are used to coat apparel interlining substrates. Interlining substrates, coated with GRILTEX adhesive products, provides fo.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
Eurofoam Porocell POR 304 CM-OPC EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
Eurofoam Porocell POR 304 CM-RS EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | Wet Service |
Chesterton ARC MXC Castable Extreme Wear Compound Description: An advanced ceramic composite, with flowable viscosity, for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It can be hand tro.. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
Eurofoam Porocell POR 304 CM EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
Eurofoam Porocell POR 304 CM-BI EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
Eurofoam Porocell POR 304 CM-KPA 45 EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
Eurofoam Porocell POR 304 CM-S EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
Eurofoam Porocell POR 304 CM-GR EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
LATI Lastil G/30 SAN, 30% Glass Fiber Reinforced Styrene-Acrylonitrile copolymer (SAN) based compound. Glass fibers. High dimensional stability. High stiffness.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaI.. |