Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K | 72.2 BTU-in/hr-ft²-°F | RT |
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 10.4 W/m-K @Temperature 100 °C |
72.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |