Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 900 °C |
177 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |