- Polymer Property : Thermal Conductivity = 132 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 132 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 19.0 W/m-K @Temperature 85.0 °C |
132 BTU-in/hr-ft²-°F @Temperature 185 °F |
|
| Indium Corp. Indalloy® 281 Bi-Sn Solder Alloy Good low melting point solder for electronics assembly of for applications where Cd and Pb are to be avoided, and for thermo-electric applications. Shear rate sensitive.Information provided by the m.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 500 °C |
132 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 85.0 °C |
132 BTU-in/hr-ft²-°F @Temperature 185 °F |
|
| Indium Corp. Indalloy® 206 Pb-In Solder Alloy Indalloy's #7, #10, #150, #204, #205 and #206 comprise a group of lead-indium solders designed to cover the temperature range of 165°C-275°C. All have the minimum gold-leaching characteristics.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | DIN EN 821-2 |
| CeramTec SL 303 Silicon Nitride, SiAION+SiC SL 303 is a silicon nitride ceramic. Silicon nitrides are ideal for components working under mechanical loads and engine parts, even and especially at elevated temperatures. Their property profile i.. |
|||
| Thermal Conductivity | 19.0 - 21.0 W/m-K | 132 - 146 BTU-in/hr-ft²-°F | after age hardening |
| EOS MS1 Maraging Steel for DMLS 3D Printing EOS Maraging Steel MS1 is a steel powder which has been optimized especially for processing on EOSINT M 270 systems. This steel has very good mechanical properties, and is easily heat-treatable us.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 100 °C |
132 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| CMT Materials METAPOR® HD 210 AL Air Permeable Material METAPOR® is a composite material made of aluminum granules and epoxy resin. The material is air-permeable over the entire surface due to its micro-porous structure allowing for unique design consi.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | |
| Bohler-Uddeholm BÖHLER S290 MICROCLEAN® High Speed Steel Description: High speed steel produced by powder-metallurgy methods with highest red hardness, compressive strength and wear resistance. The PM technology imparts to the material also excellent toug.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | |
| Bohler-Uddeholm BÖHLER S601 (M2 Modified) High Speed Steel For Cold Work Applications Properties: Tungs ten-molybdenum high speed steel with ex cel lent toughness and cut ting proper ties, for a wide variety of uses.Applications: Taps, twist drills, reamers, broaching tools, meta.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | |
| ATI Allegheny Ludlum AL 2205™ Duplex Stainless Steel, Sheet and Strip < 0.1875", UNS S31803 Ferromagnetic. The AL 2205 alloy is a nitrogen-enhanced duplex stainless steel alloy. The nitrogen serves to significantly improved the corrosion resistance of the alloy; especially in the welded c.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a.. |
|||