- Polymer Property : Thermal Conductivity = 24.0 W/m-K
Polymer Property : Thermal Conductivity = 24.0 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | DIN EN 821-2 |
| CeramTec B 601 Alumina, 98.5% Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures. |
|||
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | ASTM-C408 |
| CeramTec Rubalit® 708 Alumina, 96% Based on 96% aluminum oxide, Rubalit® 708 was developed specifically for making heavy-duty resistors and miniature metal layer resistors. Because of its outstanding strength, this same material is .. |
|||
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | DIN EN 821-2 / ASTM-C408 |
| CeramTec Rubalit® 708S Alumina, 96% Rubalit® 708S (96%) is an alumina that features high strength and thermal conductivity. It provides outstanding results when used on commercially available thick-film pastes and metallization syste.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 20.0 - 100 °C |
167 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
| CeramTec Rubalit® A 1896 brown Alumina CeramTec AG's seal and regulator discs are made mainly of Rubalit® A 1896, a material developed especially for this application that is noted for the following special properties: outstanding hard.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||