Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 17.5 W/m-K @Temperature 400 °C |
121 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
Thermal Conductivity | 17.5 W/m-K | 121 BTU-in/hr-ft²-°F | |
Special Metals MONEL® Alloy K-500 A precipitation-hardenable nickel-copper alloy that combines the corrosion resistance of MONEL alloy 400 with greater strength and hardness. It also has low permeability and is nonmagnetic to under.. |