Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 13.1 W/m-K @Temperature 200 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 200 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 200 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 200 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K | 90.9 BTU-in/hr-ft²-°F | |
California Fine Wire Stablohm 800 Nickel, Chromium, Aluminum, and Copper Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 200 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 200 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |