Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 8.20 µm/m-°C | 4.56 µin/in-°F | at Set Pt. (Fired Thermal Expansion) |
Ferro CF 7583 Low-Temperature Sealing DEVITRIFYING Typical Powder Form: TF Ferro's line of low-temperature sealing glasses are comprised of lead-borate (vitreous) and lead-zinc-borate crystallizing glasses formulated to meet specific t.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 260 °C |
4.56 µin/in-°F @Temperature 500 °F |
Fired Thermal Expansion |
Ferro CF 7583 Low-Temperature Sealing DEVITRIFYING Typical Powder Form: TF Ferro's line of low-temperature sealing glasses are comprised of lead-borate (vitreous) and lead-zinc-borate crystallizing glasses formulated to meet specific t.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 260 °C |
4.56 µin/in-°F @Temperature 500 °F |
|
Ferro EG 2927 Metal Sealing Glass Type: Sr-B-Al Typical Powder Form: VSD Typical Application: Comp. - Battery Ferro Metal Sealing glasses are formulated for sealing a wide range of metal packages and parts, including matched .. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 20.0 °C |
4.56 µin/in-°F @Temperature 68.0 °F |
|
Sapco 98% Aluminum Oxide Information provided by Sapco. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
CoorsTek AD-94 Alumina (nom. 94% Al2O3) Thermal Shock Delta Tc = 250°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
CoorsTek AD-96 Alumina (nom. 96% Al2O3) Thermal Shock Delta Tc = 250°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
CoorsTek AD-995 Alumina (nom. 99.5% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek AD-996 99.6% Alumina |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
CoorsTek AD-998 Alumina(nom. 99.8% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek ADD-96 96% Alumina |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek CAP 3 99.5% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek CAP 4 98.5% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek FG-98 98% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
CoorsTek FG-995 Alumina (nom. 98.5% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
CoorsTek PlasmaPure™ Alumina (nom. 99.8% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek PlasmaPure-UC™ 99.9% Alumina |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 |
CoorsTek Z-PLUS™ 94 Zirconia-Impr. Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 20.0 - 650 °C |
4.56 µin/in-°F @Temperature 68.0 - 1200 °F |
|
Du-Co Ceramics DC-10-L-3 Steatite Properties reported below are averages from unglazed specimens. Tests performed to ASTM specifications. Actual values may vary. Information provided by DU-CO Ceramics Company. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Astro Met AmAlOx 68 Alumina - Aluminum Oxide General Description:AmAlOx 68 alumina (Astro Met Aluminum Oxide) is a high purity 99.8% aluminum oxide (alumina) ceramic which has been developed and optimized for maximum wear resistance and corros.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 20.0 - 1000 °C |
4.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
Ceradyne Ceralloy® 225 Titanium Diboride Features:electrical conductancewear resistancehardnessApplications:wear componentsballistic armorsputtering targetsInformation provided by Ceradyne Company |
|||
CTE, linear | 8.20 µm/m-°C | 4.56 µin/in-°F | |
Poco Graphite TM Industrial Grade Graphite POCO’s specialty graphite materials are used in a wide range of highly technical and industrial applications. Each grade has characteristics and properties that allow the user to match the ideal gr.. |
|||
CTE, linear | 8.20 µm/m-°C @Temperature 20.0 - 1000 °C |
4.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
CeramTec 433 Alumina, 99.9% 433 (99.9%) is an alumina that exhibits high hardness. Its fine, equiaxial microstructure provides excellent sliding and abrasive wear resistance. This material is ideal for corrosive conditions. A .. |