Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.72 µin/in-°F @Temperature 68.0 - 212 °F |
|
Special Metals MONEL® Alloy 400 A nickel-copper alloy with high strength and excellent corrosion resistance in a range of media including sea water, hydrofluoric acid, sulfuric acid, and alkalis. Used for marine engineering, chem.. |
|||
CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 300 °C |
7.75 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schmolz + Bickenbach LeanDupâ„¢ 35N Stainless Steel Bar Description: LeanDupâ„¢ 35N also known as (Uranus 35 N) is a dual phase austentic-ferritic stainless steel that has the ability to become as important as 316L. It offers better corrosion resistan.. |
|||
CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 500 °C |
7.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
Wieland Porta SMK 82 PFM Alloy Gold-palladium ceramic alloyApplications: crowns, short span bridges, long span bridges, telescopic and milling work, removable partials, ceramic veneering, acrylic veneeringDental |
|||
CTE, linear | 13.9 µm/m-°C @Temperature 21.1 - 93.3 °C |
7.70 µin/in-°F @Temperature 70.0 - 200 °F |
|
Carlson C 400 Nickel-Copper Alloy General DescriptionCarlson Alloy C 400 is a nickel-copper alloy which provides an excellent combination of high strength, ductility, good weldability, and resistance to corrosion over a wide range o.. |
|||
CTE, linear | 13.9 µm/m-°C @Temperature 20.0 °C |
7.72 µin/in-°F @Temperature 68.0 °F |
alloy 600 property |
Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate Top layer of side 2: alloy 600 foil; Bottom layer of side 2: cured silicone rubber; Substrate is 7628 fiberglass; Side 1: cured silicone rubber |
|||
CTE, linear | 13.9 µm/m-°C @Temperature 20.0 °C |
7.70 µin/in-°F @Temperature 68.0 °F |
|
Aremco AREMCOLOX™ 502-676 Machinable Magnesium Oxide Full-fired, fine grain, high purity MgO ceramic. Inert to molten metals, slags, superconductors. Broad line of standard crucibles. Custom parts made to print. |