- Polymer Property : CTE, linear = 11.0 µm/m-°C
Polymer Property : CTE, linear = 11.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 - 500 µm/m-°C @Temperature 55.0 - 250 °C |
6.11 - 278 µin/in-°F @Temperature 131 - 482 °F |
Average value: 122 µm/m-°C Grade Count:8 |
| Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are.. |
|||
| CTE, linear | 11.0 µm/m-°C | 6.11 µin/in-°F | DIN 53752 |
| Lehmann & Voss LUVOCOM® 20-0951 Polyphthalamide, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita.. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 °C |
6.10 µin/in-°F @Temperature 68.0 °F |
|
| SGL Carbon Group Ridurid® EK 60 High Performance Graphite Filled Plastic Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 °C |
6.11 µin/in-°F @Temperature 68.0 °F |
|
| Saint-Gobain Micaver® Glass-Mica Electrical Insulator, Compression Moldings Glass-mica compound that occupies a place between plastics and ceramics in terms of usage temperature. It can be molded and machined like plastics and has the mechanical properties (strength, hardn.. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 750 °C |
6.11 µin/in-°F @Temperature 68.0 - 1380 °F |
BSÂ 1902: section 5.3: 1990 |
| Skamol Group SKAMOLEX V-1100 (700) Panel Design SKAMOLEX panel designs have the following characteristics: Max. service temperature: Up to 1150°C (2102°F)Hot-face applications or back-up insulationA large variety of specialized and versatil.. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 750 °C |
6.11 µin/in-°F @Temperature 68.0 - 1380 °F |
BSÂ 1902: section 5.3: 1990 |
| Skamol Group V-1100 375 Vermiculite Insulating Slab SKAMOL V-1100 & VIP-12 vermiculite slabs have the following characteristics: Max. service temperature: Up to 1150°C (2102°F)Hot-face applications or back-up insulation of all refractory constr.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Butyrate 485A2R30016 Natural Cellulose Acetate Butyrate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.TENITE cellulosic plastics are noted for their excellent balance of properties - toughness,.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Butyrate 530A3720016 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 12%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Butyrate 550E2R30010 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 10%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Butyrate 565A2R30016 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 10%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Propionate 371A2R30009 Natural, Trsp Cellulose Acetate Propionate Plasticizer 9%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Propionate 375E4000012 Clear, Trsp Cellulose Acetate Propionate Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Propionate 376E4000012 Clear, Trsp Cellulose Acetate Propionate Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Propionate 384A4000016 Clear, Trsp Cellulose Acetate Propionate Plasticizer 16%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 199 °C |
6.10 µin/in-°F @Temperature 68.0 - 390 °F |
|
| EDRO EDRO400™ #40 Prehardened Insert Quality Martensitic Stainless Steel EDRO400™ is a remelted 400 series martensitic stainless steel supplied prehardened to 40 HRC (375 HB).EDRO400™ is characterized by excellent polishability, superior corrosion resistance, high leve.. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 200 °C |
6.11 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Crucible Steel CPM® S30V® Stainless Steel CPM S30V is a martensitic stainless steel designed to offer the best combination of toughness, wear resistance and corrosion resistance. Its chemistry has been specially balanced to promote the form.. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 200 °C |
6.11 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Crucible Steel CPM® S90V® (420V®) Tool Steel CPM S90V is a unique tool steel made by the Crucible Particle Metallurgy process. It is a martensitic stainless steel with a high volume of vanadium carbides for exceptionally good wear resistance. .. |
|||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 °C |
6.11 µin/in-°F @Temperature 68.0 °F |
Warp |
| Cytec Thornel® Graphite Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature.. |
|||
| CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
| Alliance A-2 Alnico Magnetic Material |
|||
| CTE, linear | 11.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
6.11 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| Ascend Performance Materials Vydyne® ECO-315 Nylon 66/6, non-halogenated, ignition resistant, DAM Vydyne® ECO315 is non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and has an Underwriters Laboratories UL 94 fla.. |
|||
| CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
| Alliance A-5 Alnico Magnetic Material |
|||
| CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
| Alliance A-5DG Alnico Magnetic Material |
|||
| CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
| Alliance A-6 Alnico Magnetic Material |
|||
| CTE, linear | 11.0 - 170 µm/m-°C | 6.11 - 94.4 µin/in-°F | Average value: 83.8 µm/m-°C Grade Count:53 |
| Overview of materials for Cellulose Acetate Propionate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Propionate, Molded". Each property range of values reported is minimum and maximum val.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Acetate 109E3V36324 Clear, Trsp Cellulose Acetate
(discontinued **) Plasticizer 24%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.2% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| CTE, linear | 11.0 µm/m-°C | 6.11 µin/in-°F | |
| Mo-Sci Corporation YB-40-I Yellow B Filter Glass Applications: Lead-free NVIS Yellow class B filter glass for incandescent light sources.Information provided by Mo-Sci Corporation. |
|||
| CTE, linear | 11.0 µm/m-°C | 6.11 µin/in-°F | |
| Mo-Sci Corporation YB-40-N Yellow B Filter Glass Applications: Lead-free NVIS Yellow class B filter glass for white LED sources.Information provided by Mo-Sci Corporation. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Butyrate 465E3720008 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 8%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
| CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Eastman Tenite Butyrate 581A3720016 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||