Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | ISO 75-C |
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | Injection; ISO 75-C |
Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 140 °C | 230 - 284 °F | Average value: 123 °C Grade Count:11 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |