Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C | 102 °F | injection molded specimen; ASTM D648 |
Phillips Sumika Marlex® CHP-015 Thermoplastic Polyolefin
(discontinued **) Applications: Driver-side air-bag coversSoft interior trimSoft touch overmoldingInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 201.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C | 102 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3720 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.17 mm |
102 °F @Thickness 0.125 in |
ISO 75 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C | 102 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3720 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.17 mm |
102 °F @Thickness 0.125 in |
ISO 75 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C | 102 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3720 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.17 mm |
102 °F @Thickness 0.125 in |
ISO 75 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C | 102 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3720 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C | 102 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3720 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.17 mm |
102 °F @Thickness 0.125 in |
ISO 75 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C | 102 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3720 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.17 mm |
102 °F @Thickness 0.125 in |
ISO 75 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.17 mm |
102 °F @Thickness 0.125 in |
ISO 75 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 39.0 °C @Thickness 3.20 mm |
102 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |