Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
RheTech Products M15P101-01A 15% Mica Reinforced Polypropylene, Black Applications: Air ducts - distributionFan shroudsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PP HBK15030 D Polypropylene, Multifiller High Gloss, Detergent Resistant Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | |
Polimeri Europa KOBLEND HI PD 41 G1 PBT+PC, 5% Glass Fiber
(discontinued **) Symbol according to ISO 1043/1: PBT+PC (GF) Elastomer modified PBT+PC blend reinforced with 5% of glass fibres, a good combination of stiffness, dimensional stability and thoughness. Main applicat.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
SABIC Innovative Plastics Cycoloy® C1100HF PC+ABS (Europe-Africa-Middle East) CYCOLOY C1100HF is the improved flow version of CYCOLOY C1100 and has been developed to better fill long and complex parts while maintaining still excellent mechanical properties. Its superior flow .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PPH T3022D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
Hyosung Topilene J945 PP J945 Injection Impact CopolymerApplications: Very large articles:Washing M/C partsIndustrial applianceCharacteristics:High flowabilityHigh stiffnessInformation provided by Hyosung Corporation |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
LG Chemical LUPOL EI5002L PP Description: Injection Molding, PP, General PurposeApplication: Automotive Interior PartsCAS: 9003-07-0 and 9002-88-4Information provided by LG Chemical |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-1,-2 |
Inno-Comp INNOPOL® CS 3-3120 B 20% Talc-Filled Polypropylene INNOPOL® CS 3-3120 B is a black colored, 20% talc-filled polypropylene compound.INNOPOL® CS 3-3120 B is a recommended for producing injection molded products where the required property is hig.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 - 125 °C | 248 - 257 °F | ASTM D1525, HDT Method B |
Loxim 840 02T HB Polypropylene Compound, 40% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
IRPC Polimaxx Polene 2300NCA Polypropylene Block Copolymer CHARACTERISTICS: HIGH STIFFNESS, HIGH IMPACT, MEDIUM FLOW, HEAT STABILITY CONTAIN UV STABILIZER ADDITIVE APPLICATIONS: INJECTION MOLDING SPECIALLY FOR BATTERY CASES, AUTOPARTS AND ELECTRICAL APPLIAN.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
IRPC Polimaxx Polene 2346NC Polypropylene Block Copolymer CHARACTERISTICS: HIGH STIFFNESS, HIGH IMPACT, MEDIUM FLOW, HEAT STABILITY CONTAIN ANTISTATIC AND UV STABILIZER ADDITIVEAPPLICATIONS: INJECTION MOLDING FOR ELECTRICAL APPLIANCES, AUTOPARTS |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | |
LATI Latene® 7H2W T-V0 PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardantsAvailability: Africa & Middle East; Asia Pacif.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D 648 |
MRC Polymers NAXALOY™ 793MF6 PC + Polyester Blend, 6% Mineral Filled • Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants can be addedInformation provided by MRC Polymers Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Valox® 359 PBT (Europe-Africa-Middle East) VALOX 359 is an unreinforced, flame retarded, low warpage PBT injection moulding resin. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
SABIC Innovative Plastics Valox® 745 PBT (Europe-Africa-Middle East) VALOX 745 is 30% mineral filled PBT injection moulding resin with improved toughness and low warpage. Applications: telephone ringer frames, card racks. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
SABIC Innovative Plastics Valox® VX5005 PBT (Europe-Africa-Middle East) VALOX VX5005 is a 5% glass fibre reinforced, impact modified PBT+PC blend with low warpage characteristics.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-2 |
Borealis Daplen™ ED206HP TPO Compound Daplen ED206HP is a 25% mineral reinforced compound intended for injection molding. ED206HP has been developed especially for the car industry, to be used in interior parts requiring excellent scra.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
Unitika TERRAMAC TE-8210 Polylactic Acid (PLA) High-durability, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | >= 120 °C | >= 248 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | DIN 53461 |
Polyram RamLloy PBB701 PC/ABS alloy, UV Stabilized UV stabilized PC/ABS alloy for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene DescriptionPolypropylene PP 3369-01 is a medium-flow homopolymer polypropylene nucleated and anti-static designed for the molding of thin walled, and large parts.ApplicationTypical applications of P.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-2 |
Borealis MS64T20 Polypropylene Compound, Mineral Filled MS64T20 is a 20% mineral filled polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and is easy to process. Applications: automotive p.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
A. Schulman PP 3482-01 Polypropylene Nucleated Homopolymer Polypropylene DescriptionPP 3482 is a nucleated homopolymer polypropylene with excellent heat resistance and stiffness properties.ApplicationThis product is for injection molded applications and is in compliance .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | |
Covestro Bayblend® T 64 Polycarbonate/ABS Blend Easier flowing than BAYBLEND T 65 MN.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-2/B |
ExxonMobil Exxtral™ HMU 301 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for high heat and discoloration resistance, good surface finish, and detergent resistance for electrical appliances such as w.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | DAM; ISO 75-1/-2 |
DuPont Performance Polymers Zytel® LC6601 NC010 Nylon 612 Plasticized Toughened Polyamide 612 Developed for Extrusion Information provided by DuPont Performance Polymers |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
Cheng Yu Plastic 3245 TPE Rubber |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
Arkema Group Rilsan® Clear G350 Polyamide Rilsan® Clear G350 is a high performance transparent polyamide. This grade has been specially designed for injection molding applications, ideally suited for optics as high end eyewear frames.Infor.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
SABIC Innovative Plastics Cycoloy® C1100 PC+ABS (Europe-Africa-Middle East) CYCOLOY C1100 is a PC+ABS blend developed to satisfy the demanding application requirements, where optimum combination is needed of superior processing efficiency, excellent ductility also at sub ze.. |