- Polymer Property : CTE, linear = 8.94 µin/in-°F
Polymer Property : CTE, linear = 8.94 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.1 - 17.1 µm/m-°C @Temperature 20.0 - 200 °C |
8.94 - 9.50 µin/in-°F @Temperature 68.0 - 392 °F |
|
| PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T6 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 500 °C |
8.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 20.0 - 980 °C |
8.94 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |
|||