- Polymer Property : CTE, linear = 8.67 µin/in-°F
Polymer Property : CTE, linear = 8.67 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.6 - 16.6 µm/m-°C @Temperature 20.0 - 200 °C |
8.67 - 9.22 µin/in-°F @Temperature 68.0 - 392 °F |
|
| PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6 Heat Treatment Condition T6 (Quench in water at RT)abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of p.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 20.0 - 700 °C |
8.67 µin/in-°F @Temperature 68.0 - 1290 °F |
|
| Haynes Hastelloy® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications includ.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, GTAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 20.0 - 100 °C |
8.67 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum 309 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 20.0 - 100 °C |
8.67 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum 309H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 20.0 - 100 °C |
8.67 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum 309S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 20.0 - 100 °C |
8.67 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum 309Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 23.0 - 400 °C |
8.67 µin/in-°F @Temperature 73.4 - 752 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 15.6 µm/m-°C @Temperature 20.0 - 870 °C |
8.67 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |
|||