Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.6 µm/m-°C @Temperature 0.000 - 800 °C |
7.56 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® STAR with P/M Processing Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy sheet Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 50% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 900 °C |
7.56 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean |
Dura-Bar 100-70-03 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 400 °C |
7.56 µin/in-°F @Temperature 68.0 - 752 °F |
|
Carpenter R.D.S.® Alloy Tool Steel (Oil-Hard) (AISI L6) R.D.S. tool steel is an oil hardening die steel which combines extreme toughness with very little size change when heat treated. It is available as a DeCarb-Free product. DCF bars have been cold fin.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 430 °C |
7.56 µin/in-°F @Temperature 68.0 - 806 °F |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |