| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.2 µm/m-°C @Temperature 0.000 - 300 °C |
6.78 µin/in-°F @Temperature 32.0 - 572 °F |
|
| Kennametal Stellite Stellite® STAR cast Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 500 °C |
6.78 µin/in-°F @Temperature 68.0 - 932 °F |
|
| International Mold Steel Daido DRM1 Matrix High-Speed Steel This tough matrix type high speed tool steel features high hardness and high tough Matrix type high speed tool steel vastly surpasses hot work die steels. DRM1 improves hot and warm die life by its .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 30% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 100 °C |
6.78 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Latrobe LSSâ„¢ 2714T Hot Work Tool Steel (DIN 1.2714 mod) TLS 2714HT is the same steel available from inventory in a heat-treated condition, at a hardness of 352 to 401 HBS (approximately 38 to 43 HRC). TLS 2714HT can be readily flame cut, and this propert.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 538 °C |
6.78 µin/in-°F @Temperature 1000 °F |
|
| Special Metals INCOLOY® alloy 908 INCOLOY® alloy 908 (UNS N09908) is an age-hardenable nickel-iron alloy which exhibits a low coefficient of thermal expansion, high tensile strength, high fracture and impact toughness, fatigue cr.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 21.0 - 300 °C |
6.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Dura-Bar 120-90-02 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 21.0 - 300 °C |
6.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Dura-Bar 60-40-18 Continuously Cast Ductile Iron Bar Stock ASTM A536, 4018 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 300 °C |
6.78 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature <=427 °C |
6.78 µin/in-°F @Temperature <=801 °F |
|
| AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 1075 AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 21.0 - 649 °C |
6.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Carpenter Micro-Melt® 9 Hardened and Tempered Tool Steel Micro-Melt® 9 tool steel is a high vanadium tool steel produced using the Carpenter Micro-Melt powder process. This grade possesses wear resistance superior to most other tool steels along with goo.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 400 °C |
6.78 µin/in-°F @Temperature 68.0 - 752 °F |
|
| Carpenter No. 610® High Carbon, High Chrome Tool Steel (Air-Wear) (AISI D2) No. 610 tool steel is an air hardening, high-carbon, high-chromium tool steel having extremely high wear resisting properties. It is very deep hardening, and will be practically free from size chang.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 500 °C |
6.78 µin/in-°F @Temperature 68.0 - 932 °F |
|
| ATI Allegheny Ludlum Stainless Steel Ohmaloy® 40 Resistance Alloy Ohmaloy 40 alloy is a moderately magnetic, ductile stainless steel having extremely high electrical resistivity. In addition to imparting high electrical resistivity, the aluminum content in these .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||